The effect of stress concentration around the hole easily leads to fatigue failure of aircraft structures, and usually causes catastrophic accidents. In order to elucidate the influence of cold expansion on the fatigue life of AA2024-T351 specimens, fatigue tests of specimens before and after cold expansion were accomplished on high frequency fatigue test machine. Combining the finite element simulation with X-ray diffraction measurement, the evolution of residual stress around the hole was thus investigated. Meanwhile, scanning electron microscope (SEM) and transmission electron microscope (TEM) were employed to observe the fatigue fracture morphology, fatigue striation and microstructure characteristics, and to explore the influence of microstructure features on fatigue life. Research results show that the cold expansion with 0.4 mm can significantly improve the fatigue resistance of AA2024-T351 specimens, and the fatigue limit can be increased by about 42%.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Influence of hole cold expansion on fatigue resistance of 2024 aluminum alloy


    Beteiligte:
    WANG Lianqing (Autor:in) / BIAN Jiang (Autor:in) / ZHANG Han (Autor:in) / WU Shengchuan (Autor:in)


    Erscheinungsdatum :

    2020




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Influence of Hole Cold Expansion on Microstructure and Fatigue Life of 2124 Aluminum Alloy

    YI Linna / RU Jigang / HUANG Min et al. | DOAJ | 2016

    Freier Zugriff

    Cold Expansion Strengthening of 7050 Aluminum Alloy Hole: Structure, Residual Stress, and Fatigue Life

    Qi Li / Qichao Xue / Quansheng Hu et al. | DOAJ | 2022

    Freier Zugriff

    Effect of Strengthened Hole on the Fatigue Life of 2024-T3 Aluminum Alloy

    Huang, Hong / Zhao, Qingyun / Liu, Fenglei | Springer Verlag | 2019


    Creep Resistance of 2024 Aluminum Alloy

    Tsai, Chih-Jrn / Wang, Le-Min / National Defense Univ. | SAE Technical Papers | 2013


    Effect of Cold Expansion on Fatigue Life of Hole Structure of TC17 Titanium Alloy

    AI Yingjun / WANG Xin / SONG Yinggang et al. | DOAJ | 2017

    Freier Zugriff