The change of fatigue life and microstructure of 2124-T851 thick plate after cold expanded with different deformation was studied by fatigue test, TEM, SEM and X-ray diffraction apparatus. The results show that the fatigue life increases with the increase of expanded deformation until the maximum value is reached, and then decreased rapidly with the increase of expanded deformation. At 0.4 mm expanded deformation, fatigue life reach peak value, which is 12.66 times of the non-cold-worked specimens. The microstructure research results show that the residual compressive stress and dislocation cell structure form around the cold-worked holes during the cold expansion, and increase quickly with the expanded deformation. The strengthened layer retarded the fatigue crack growth rate. The appropriate cold expanded deformation can improve the surface roughness of hole, and retard the initiation of fatigue crack, consequently improving the whole fatigue life.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Influence of Hole Cold Expansion on Microstructure and Fatigue Life of 2124 Aluminum Alloy


    Beteiligte:
    YI Linna (Autor:in) / RU Jigang (Autor:in) / HUANG Min (Autor:in) / SONG Deyu (Autor:in) / WANG Liang (Autor:in)


    Erscheinungsdatum :

    2016




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Aluminum Alloy 2124, Plate

    SAE Technical Papers | 2007


    Aluminum Alloy 2124, Plate

    SAE Technical Papers | 2013


    Influence of hole cold expansion on fatigue resistance of 2024 aluminum alloy

    WANG Lianqing / BIAN Jiang / ZHANG Han et al. | DOAJ | 2020

    Freier Zugriff

    Cold Expansion Strengthening of 7050 Aluminum Alloy Hole: Structure, Residual Stress, and Fatigue Life

    Qi Li / Qichao Xue / Quansheng Hu et al. | DOAJ | 2022

    Freier Zugriff