A new class of large, high-speed seagoing ferry-boat is under development for service around the world. The ships, which are built entirely of aluminum-alloy plate and stiffeners, show a propensity for fatigue cracking of the welded structure. Cracks may occur in both the hulls and the superstructure early in their 20-year service life. Early appearance of fatigue cracks is shown to result from the combined stress and strain fields set up in weld zones by the static residual stresses and cyclic loads, beyond the effects of weld and detail geometry. A numerical example demonstrates that conventional methods of fatigue analysis overestimate the lifetime of the welded aluminum structure, while damage tolerance analysis based on fracture mechanics leads to improved prediction.
Considerations of the effect of residual stresses on fatigue of welded aluminum alloy structures
Fatigue and Fracture of Engineering Materials and Structures ; 21 , 2 ; 159-170
1998
12 Seiten, 24 Quellen
Article (Journal)
English
Residual stresses in welded structures
Engineering Index Backfile | 1942
|Residual stresses in welded structures
Tema Archive | 2008
|Effects of residual stresses on the fatigue behaviour of welded steel structures
Tema Archive | 2005
|Fatigue Endurance of Welded Joints, Residual Stresses and Fatigue Improvement Treatments
British Library Conference Proceedings | 1993
|Residual stresses in welded ships
Engineering Index Backfile | 1942
|