Today most instrument panels and interior padded parts are made of polyurethane foam covered with a polyvinyl chloride (PVC) skin. A key concern in the industry is the long-term appearance of the interior parts. Recent automotive designs have resulted in more pronounced windshield angles and increased surface areas of the instrument panel exposed to direct sunlight. A consequence of these design features is closed car interior temperatures approaching 120 Cel. The resulting thermal and light stress causes many instrument panels to discolor and crack. Previous studies have shown that vinyl staining is the result of dehydrochlorination of the PVC which is manifested as color changes as well as cross-linking of PVC, and foam degradation. In this study, the results of heat aging tests at 149 Cel indicate that colorimetric testing is a reliable and objective method of monitoring stain development. Using this procedure, it was seen that different catalysts in urethane foam formulations can dramatically affect the staining characteristics of vinyl surfaces.
Polyurethane foam catalysts for applications in non-staining instrument panels
Polyurethanschaumkatalysatoren für licht- und wärmebeständige Instrumententafeln
SAE-Papers ; Mar ; 1-6
1990
6 Seiten, 6 Bilder, 1 Tabelle, 16 Quellen
Conference paper
English
Polyurethane Foam Catalysts for Applications in Non-Staining Instrument Panels
SAE Technical Papers | 1990
|Polyurethane foam catalyst for applications in non-staining instrument panels
Automotive engineering | 1990
|The influence of polyurethane foam on the heat staining of instrument panels
Tema Archive | 1988
|The influence of polyurethane foam on the heat staining of instrument panels
Automotive engineering | 1988
|The Influence of Polyurethane Foam on the Heat Staining of Instrument Panels
SAE Technical Papers | 1988
|