The European directive 2000/53/EC limits the use of Cr(VI) in vehicle manufacturing. Although a maximum of 2 g of Cr(VI) was authorised per vehicle for corrosion prevention coatings of key components, since July 2007 its use has been prohibited except for some particular applications. Therefore, the objective of the study was to develop direct analytical procedures for Cr(VI) determination in the different steel coatings used for screws. Instead of working directly with screws, the optimisation of the procedures was carried out with metallic plates homogeneously coated to improve the data comparability. Extraction of Cr(VI) from the metallic parts was performed by sonication. Two extraction solutions were tested: a direct water extraction solution used in standard protocols and an ammonium/ammonia buffer solution at pH 8.9. The extracts were further analysed for Cr speciation by high-performance liquid chromatography (HPLC) inductively coupled plasma (ICP) atomic emission spectrometry or HPLC ICP mass spectrometry depending on the concentration level. When possible, the coatings were also directly analysed by solid speciation techniques (X-ray photoelectron spectroscopy, XPS, and X-ray absorption near-edge structure, XANES) for validation of the results. Very good results between the different analytical approaches were obtained for the sample of coating made up of a heated paint containing Zn, Al and Cr when using the extracting buffer solution at pH 8.9. After a repeated four-step extraction procedure on the same portion test, taking into account the depth of the surface layer reached, good agreement with XPS and XANES results was obtained. In contrast, for the coatings composed of an alkaline Zn layer where Cr(VI) and Cr(III) are deposited, only the extraction procedure using water allowed the detection of Cr(VI). To elucidate the Cr(VI) reduction during extraction at pH 8.9, the reactivity of Cr(VI) towards different species of Zn generally present in the coatings (metallic Zn and zinc oxide) was studied. The results showed that metallic Zn rapidly reduces Cr(VI), whereas this reaction is less evident in the presence of zinc oxide. Water was then retained for coatings containing metallic Zn.
Development of analytical procedures for the determination of hexavalent chromium in corrosion prevention coatings used in the automotive industry
Entwicklung eines analytischen Verfahrens zur Bestimmung von Chrom(VI) in Korrosionsschutz-Beschichtungen, die in der Automobilindustrie verwendet werden
Analytical and Bioanalytical Chemistry ; 391 , 2 ; 587-597
2008
11 Seiten, 4 Bilder, 6 Tabellen, 41 Quellen
Article (Journal)
English
Hexavalent chromium determination on anti-corrosion zinc based coatings
SAE Technical Papers | 2009
|Development of Hexavalent Chromium-free Surface Treatment
British Library Conference Proceedings | 2005
|Development of hexavalent chromium-free surface treatment
Automotive engineering | 2005
|Development of Hexavalent Chromium-free Surface Treatment
SAE Technical Papers | 2005
|Corrosion Prevention of Safety Critical Components in the Automotive Industry
British Library Conference Proceedings | 1996
|