The present paper outlines twin roll casting followed by hot rolling to produce magnesium alloy sheet as an alternative to classical production via DC casting and hot rolling or continuous casting. Results and evaluations from trials with semi-scale twin roll cast and hot rolled AZ31B are presented. Strip of 4.5mm thickness and up to 650mm width has been cast at casting speeds between 1.0 m/min and 2.0 m/min. After the twin roll casting, the sheets were hot rolled down to 1.5mm final gauge on a semiscale hot mill. Rolling temperature was chosen between 350 C and 400 C deg. In the as-cast TRC condition a typical grain size of 200-400 micrometer can be achieved without any added grain refinement; additionally, a relatively small cell (sub-grain) size of 6-7 micrometer was measured. This grain structure is in contrast to samples from DC cast slabs showing a grain size of 1-2 mm when no grain refinement is used. After preheating prior to hot rolling, a significant grain refinement was noted, indicating a severe plastic deformation within the roll/casting gap and subsequent recrystallization. After hot rolling with several passes and reheating steps, samples were again taken for metallographic investigation. Gauges of 3mm, 2.5mm and 1.5mm were successively examined. After rolling to the intermediate gauges of 3.0mm and 2.5mm, the deformation energy was insufficient for complete recrystallization during subsequent annealing. Thus, it can be concluded that a relative reduction of >60% is necessary to achieve a homogeneous fine-grained microstructure. At 1.5mm a mean grain size of about 10 micrometer can be achieved, which is a distinctive feature in comparison with sheet produced via the classical route of DC casting and hot rolling, where grain sizes of 20-50 micrometer are common. After standard tensile testing of specimens, the yield strength reaches values in the final gauge (1.5mm) of 215MPa and 235MPa in the longitudinal and transverse directions. For the surface roughness (Ra), values of about 1 micron for the as-cast condition and typically 0.3 and 0.2 micron for the hot rolled condition in the transverse and longitudinal directions, respectively, were determined.


    Access

    Access via TIB

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    An efficient route to magnesium alloy sheet: Twin roll casting and hot rolling


    Contributors:


    Publication date :

    2005


    Size :

    11 Seiten, 7 Bilder, 6 Quellen



    Type of media :

    Conference paper


    Type of material :

    Print


    Language :

    English





    Performance of Electromagnetic Purification System in Continuous Twin Roll Casting of Aluminium Sheet

    Shu, D. / Wang, J. / Sun, B. D. | British Library Conference Proceedings | 2007


    Hot Rolling of AZ31 Magnesium Alloy to Sheet Gauge

    Galvani, Claude / Essadiqi, Elhachmi / Shen, Guowu et al. | SAE Technical Papers | 2006


    Study on Solidification Microstructure of AZ31 Alloy Strips by Vertical Twin Roll Casting

    Wang, J. / Jiang, B. / Ding, P. D. et al. | British Library Conference Proceedings | 2007


    Hot rolling of AZ31 magnesium alloy to sheet gauge

    Essadiqi,E. / Galvani,C. / Verma,R. et al. | Automotive engineering | 2006