Measurements are reported of the absorption intensity due to the 4I11/2=4F3/2 transition in various Nd-doped silicate and phosphate laser glasses. The temperature range was 300-720K. Stimulated emission cross-sections were calculated and compared with other data, indicating that the integrated intensity of the 4F3/2=4I11/2 transition was almost independent of the population of Stark levels involved.


    Access

    Access via TIB

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    Determination of the stimulated emission cross section of neodymium glasses by measurement of the absorption from the thermally populated 4I11/2 levels


    Additional title:

    Bestimmung des stimulierten Emissionsquerschnittes von Laserglaesern durch Messung der Absorption von thermisch besetzten <sup>4</sup>I<sub>11/2</sub>- Niveaus


    Contributors:

    Published in:

    Publication date :

    1977


    Size :

    4 Seiten, 14 Quellen




    Type of media :

    Article (Journal)


    Type of material :

    Print


    Language :

    English




    Effective stimulated emission and excited-state absorption cross-section spectra of para-phenylene-ethynylene polymers

    Holzer, W. / Penzkofer, A. / Gong, S.-H. et al. | British Library Online Contents | 1998


    Disordered Nd:LuYSiO5 crystal lasers operating on the 4F3/2 → 4I11/2 and 4F3/2 → 4I13/2 transitions

    Guan, Xiaofeng / Zhou, Zhiyong / Huang, Xiaoxu et al. | British Library Online Contents | 2017


    Disordered Nd:LuYSiO5 crystal lasers operating on the 4F3/2 → 4I11/2 and 4F3/2 → 4I13/2 transitions

    Guan, Xiaofeng / Zhou, Zhiyong / Huang, Xiaoxu et al. | British Library Online Contents | 2017


    Er3+-doped fluorozirconate glass modified by PbF2 with high stimulated emission cross-section

    Xue, Tianfeng / Huang, Chunlei / Wang, Longfei et al. | British Library Online Contents | 2018


    Er3+-doped fluorozirconate glass modified by PbF2 with high stimulated emission cross-section

    Xue, Tianfeng / Huang, Chunlei / Wang, Longfei et al. | British Library Online Contents | 2018