In this investigation, dissimilar 5754/7075 and 7075/5754 spot friction welds were first made under different processing conditions. The spot friction welds in lap-shear specimens were tested under quasi-static loading conditions. The optimal processing times to maximize the failure loads of the 5754/7075 and 7075/5754 welds under lap-shear loading conditions are identified. The maximum failure load of the 7075/5754 welds is about 40% larger than that of the 5754/7075 welds. Optical micrographs of both types of spot friction welds made at different processing times before and after failure are examined. The micrographs show different weld geometries and different failure modes of spot friction welds made at different processing times. The failure modes of the 5754/7075 and 7075/5754 spot friction welds appear to be quite complex and strongly depend on the geometry and the strength of the interfacial surface between the two deformed sheet materials.


    Access

    Check access

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    Effects of Processing Time on Strengths and Failure Modes of Dissimilar 5754/7075 and 7075/5754 Spot Friction Welds in Lap-Shear Specimens


    Additional title:

    Sae Technical Papers


    Contributors:
    Pan, Jwo (author) / Pan, Tsung-Yu (author) / Tran, Van-Xuan (author)

    Conference:

    SAE World Congress & Exhibition ; 2008



    Publication date :

    2008-04-14




    Type of media :

    Conference paper


    Type of material :

    Print


    Language :

    English





    Fatigue Behavior of Dissimilar 5754/7075 and 7075/5754 Spot Friction Welds in Lap-Shear Specimens

    Pan, Jwo / Pan, Tsung-Yu / Tran, Van-Xuan | SAE Technical Papers | 2010


    Fatigue behaviors of aluminum 5754-O spot friction welds in lap-shear specimens

    Tran,V.X. / Pan,J. / Pan,T.Y. et al. | Automotive engineering | 2008


    Fatigue Behaviors of Aluminum 5754-O Spot Friction Welds in Lap-Shear Specimens

    Pan, Jwo / Pan, Tsung-Yu / Tran, Van-Xuan | SAE Technical Papers | 2008


    Microstructures and Failure Mechanisms of Spot Friction Welds in Lap-Shear Specimens of Aluminum 5754 Sheets

    Pan, J. / Santella, M. L. / Lin, P.-C. et al. | SAE Technical Papers | 2005