Failure mode and fatigue behavior of dissimilar laser welds in lap-shear specimens of aluminum and copper sheets are investigated. Quasi-static tests and fatigue tests of laser-welded lap-shear specimens under different load ranges with the load ratio of 0.1 were conducted. Optical micrographs of the welds after the tests were examined to understand the failure modes of the specimens. For the specimens tested under quasi-static loading conditions, the micrograph indicates that the specimen failed through the fusion zone of the aluminum sheet. For the specimens tested under cyclic loading conditions, two types of failure modes were observed under different load ranges. One failure mode has a kinked crack initiating from the interfacial surface between the aluminum and copper sheets and growing into the aluminum fusion zone at an angle close to 90°. The other failure mode has an interfacial crack initiating at the interfacial surface between the aluminum and copper sheets and growing along the interfacial surface between the fusion zone and the copper base metal at an angle close to 90°. In general, the fatigue lives are longer for the specimens failed through the copper sheet than those failed through the aluminum fusion zone.


    Access

    Check access

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    Failure Mode and Fatigue Behavior of Dissimilar Laser Welds in Lap-Shear Specimens of Aluminum and Copper Sheets


    Additional title:

    Sae Int. J. Mater. Manf
    Sae International Journal of Materials and Manufacturing


    Contributors:
    Pan, Jwo (author) / Sung, Shin-Jang (author) / Lai, Wei-Jen (author) / Su, Xuming (author) / Guo, Yunan (author)

    Conference:

    SAE 2014 World Congress & Exhibition ; 2014



    Publication date :

    2014-04-01


    Size :

    5 pages




    Type of media :

    Conference paper


    Type of material :

    Print


    Language :

    English