Weld lines occur when melt flow fronts meet during the injection molding of plastic parts. It is important to investigate the weld line because the weld line area can induce potential failure of structural application. In this paper, a weld line factor (W-L factor) was adopted to describe the strength reduction to the ultimate strength due to the appearance of weld line. There were two engineering thermoplastics involved in this study, including one neat PP and one of talc filled PP plastics. The experimental design was used to investigate four main injection molding parameters (melt temperature, mold temperature, injection speed and packing pressure). Both the tensile bar samples with/without weld lines were molded at each process settings. The sample strength was obtained by the tensile tests under two levels of testing speed (5mm/min and 200mm/min) and testing temperatures (room temperature and -30°C). The results showed that different materials had various values of W-L factor. For neat PP, the W-L factor was high and independent to injection molding parameters or testing temperatures. For the talc filled PP, the W-L factor reduced significantly and was not sensitive to the injection molding parameters or testing speed. The talc particles played dominant role in reducing the W-L factor. The influence of packing pressure could be ignored.
Weld Line Factors for Thermoplastics
Sae Technical Papers
WCX™ 17: SAE World Congress Experience ; 2017
2017-03-28
Conference paper
English
British Library Online Contents | 2015
British Library Online Contents | 2015
Recycling engineering thermoplastics
Online Contents | 1994
Automotive engineering | 1983
|Emerald Group Publishing | 1944
|