Heterojunction solar cells of p ‐type cupric oxide (CuO) and n ‐type silicon (Si), p ‐CuO/ n ‐Si, have been fabricated using conventional sputter and rapid thermal annealing techniques. Photovoltaic properties with an open‐circuit voltage ( V oc ) of 380 mV, short circuit current ( J sc ) of 1.2 mA/cm 2 , and a photocurrent of 2.9 mA/cm 2 were observed for the solar cell annealed at 300 °C for 1 min. When the annealing duration was increased, the photocurrent increased, but the V oc was found to reduce because of the degradation of interface quality. An improvement in the V oc resulting to a record value of 509 mV and J sc of 4 mA/cm 2 with a high photocurrent of ~12 mA/cm 2 was achieved through interface engineering and controlling the phase transformation of CuO film. X‐ray diffraction, X‐ray photoelectron spectroscopy, and high‐resolution transmission electron microscopy analysis have been used to investigate the interface properties and crystal quality of sputter‐deposited CuO thin film. The improvement in V oc is mainly due to the enhancement of crystal quality of CuO thin film and interface properties between p ‐CuO and n ‐Si substrate. The enhancement of photocurrent is found to be due to the reduction of carrier recombination rate as revealed by transient photovoltage spectroscopy analysis. Copyright © 2014 John Wiley & Sons, Ltd. Heterojunction solar cells of p ‐type cupric oxide (CuO) and n ‐type silicon (Si), p ‐CuO/ n ‐Si, have been fabricated using conventional sputter and rapid thermal annealing techniques. The presence of thin interfacial layer at the heterojunction is mainly responsible for the degradation of device performance. An improvement in the V oc resulting to a record value of 509 mV and Jsc of 4 mA/cm 2 with a high photocurrent of ~12 mA/cm 2 was achieved through interface engineering by controlling the working pressure during sputter deposition.


    Access

    Access via TIB

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    p‐CuO/n‐Si heterojunction solar cells with high open circuit voltage and photocurrent through interfacial engineering



    Published in:

    Publication date :

    2015




    Type of media :

    Article (Journal)


    Type of material :

    Print


    Language :

    English



    Classification :

    BKL:    53.36 Energiedirektumwandler, elektrische Energiespeicher