Composite structures have become popular in modern aircraft because they help reduce weight and increase durability. In addition, hat-stiffened panels provide the stability that the airframe skin needs. However, they can be subject to delamination in the post-buckling regime. Progressive damage analysis (PDA) methods can help predict interlaminar and intralaminar failure events. Many aircraft structures are subject to cyclic loading in the post-buckling regime. Hence, fatigue life prediction becomes essential for design and sustainment purposes. Under the NASA Advanced Composites Project (ACP), composite panels stiffened with single hat-stringers were subject to a cyclic loading sequence from a pre-buckling state to a post-buckling state. This test campaign aimed to provide damage initiation and growth data for three initial damage scenarios: nominally pristine, initial Teflon inserts representing manufacturing defects, and impact-induced damage. This work uses the Abaqus FEA Virtual Crack Closure Technique (VCCT), capabilities enhanced through a novel empirical method integrating fatigue R-curve effects (different from R-ratio) into the Paris Law via user-defined subroutine to simulate the fatigue response of the panels with single hat-stringers. The analysis predictions were within 5% of the test results using this novel method.


    Access

    Access via TIB

    Check availability in my library


    Export, share and cite



    Title :

    Integration of Fatigue R-Curve Effects into VCCT for Durability Predictions, Part 1: Buckled Composite Single-Stringer Stiffened Panels


    Contributors:

    Conference:

    AIAA SciTech 2023 ; 2023 ; National Harbor, MD, US


    Type of media :

    Conference paper


    Type of material :

    No indication


    Language :

    English