Entstehung und Ausbreitung von Dauerschwingrissen in fehlerhaften Punktschweißverbindungen aus 2 mm dicken AlCuMg-Blechen. Die bei dynamischer Belastung zum Bruch führenden Dauerschwingrisse entstehen am Schweißlinsenrand. Mit Zeitraffung.
The film shows the formation and the propagation of fatigue cracks in defective spot welds of 2 mm sheets of AlCuMg2 pl. The crack propagation under dynamic load has been filmed by time-lapse photography. The specimens were illuminated by a stroboscope. The film demonstrates that fatigue cracks always start at the margin of the defective spotwelds without regard to the size and orientation of defects in the weld nugget. In two of the five defective weld nuggets being analyzed hot cracks did not propagate during the whole cyclic-load time. In the other defective spot weldings the hot cracks propagated after the fatigue cracks from the margin of the weld nugget had propagated over a distance greater than the single sheet-thickness.
Werkstoffermüdung - Rißausbreitung an Punktschweißungen von Aluminiumblechen im Dauerschwingversuch
Documentation/Report
Fatigue Test - Fissure Formation in Welded Spots of Aluminium Sheets during Endurance Test Oscillations
1972-01-01
40MB, 00:03:17:16
Stummfilm
Silent movie
Audio-visual
Audio-visual
Unknown
Legierung / Aluminiumlegierung , Aluminiumlegierung / Bruchvorgang , Werkstoffermüdung / Aluminiumblech , Aluminiumlegierung / Schwingbeanspruchung , Schweißverbindung, fehlerhafte , Technik , Werkstoffwissenschaften , Werkstoffeigenschaften der Metalle alloy / aluminium alloy , aluminium alloy / breaking process , fatigue of material / aluminium sheet , aluminium alloy / oscillation stress , welded joint, defective , Encyclopaedia Cinematographica , technology , material sciences , material properties of metals
Charakterisierung der interlaminaren Werkstoffermüdung von CFK
IuD Bahn | 2002
|LAGER - Unterschiedliche Arten der Werkstoffermüdung von Wälzlagern
Online Contents | 1999
|Bandbeschichtung von Aluminiumblechen
Automotive engineering | 2004
|Plasmapulververbindungsschweißen von Aluminiumblechen
IuD Bahn | 2004
|Laserstrahlschweißen von Aluminiumblechen
IuD Bahn | 1997
|