In the exploration of icy ocean worlds, including Enceladus, Europa, and Titan, the absence of information related to material properties of the surface requires that sampling subsystems possess a robust capability to interact with a broad variety of potential icy terrain scenarios. To aid in the development of sampling subsystems that can navigate the challenges of surface excavation, sample collection, and sample delivery in a variety of terrain conditions, we aim to reproducibly generate plausible solid icy simulants with a range of mechanical properties at a scale relevant to the activities of sampling tools testbeds. This paper presents a simple method for relatively large-scale (kg/hr) manufacturing of granular ice based on a flash-freezing process that enables entrapment of additives within the ice particulates at the micron-scale. Employing additives based on magnesium sulfate (MgSO4) as an exemplary system applicable to Europa, we explore the impact of post-manufacturing densification parameters on granular ice mechanical properties. Simulants are characterized via porosity, concentration uniformity, qualitative assessment of particle characteristics, Raman spectroscopy, and mechanical properties testing (Shore A hardness and 3-point-bend). Our granular ice manufacturing process was found to produce roughly 17 kg of granular ice with MgSO4-based additives in a 2–3 hour time span. The concentration of MgSO4 was uniform at the gram-scale, and average particle diameters of granular ice as-manufactured ranged from 169 μm - 317μm. Raman spectroscopy indicated the formation of a glassy phase of MgSO4 hydrate when freshly frozen, and in consistency with literature, storage at low temperatures and subsequent (unintentional) thermal cycling resulted in the formation of epsomite (MgSO4•7H2O) (MS7) and mixed MS7+meridianiite (MgSO4•11H2O) (MS11) phases, respectively. Densification was accomplished using both small (commissioning) and large (scale of sampling activities) press molds. A test matrix generated via Design of Experiments (DoE) was used to explore the impact of time (7 days and 21 days), temperature (−10°C, −40°C, −80°C), pressure (1 MPa and 27 MPa), and MgSO4 concentration (0.0 wt.%, 2.3 wt.%, and 16.0 wt.%); simulants with a range of spatially uniform mechanical properties (1–72 Shore A hardness, and 39–51% porosity) were produced. Images of densified particles revealed that melting was likely the primary mechanism of densification, and MgSO4 phase characteristics suggested that formation of MS11 during densification was promoted by high MgSO4 concentrations and high temperatures. Temperature had the highest impact on Shore A hardness. Future work aims to broaden the range of accessible simulant mechanical properties by varying granular ice particle diameter and expanding the densification parameter space. Ultimately, a range of densified samples will be tested with sampling tools and systems to understand the unique ways in which various simulant mechanical properties pose unique sample excavation, collection, and delivery challenges.


    Access

    Check access

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    Manufacturing and Characterization of Icy Simulants for Europa


    Contributors:


    Publication date :

    2023-03-04


    Size :

    4414354 byte




    Type of media :

    Conference paper


    Type of material :

    Electronic Resource


    Language :

    English



    MANUFACTURING AND CHARACTERIZATION OF LUNAR REGOLITH SIMULANTS

    Celik, Kemal / Hay, Rotana / Peng, Bo | TIBKAT | 2022


    Lunar Simulants

    Edmunson, Jennifer E. | NTRS | 2018


    Manufacturing High-Fidelity Lunar Agglutinate Simulants

    Gutafson, R. J. / Edmunson, J. E. / Rickman, D. L. | NTRS | 2010


    Characterization and Evaluation of Lunar Regolith and Simulants

    Cross, William M. / Murphy, Gloria A. | NTRS | 2010


    Spectroscopic Characterization of Reactions Involving Counter-WMD Simulants

    Niemiec, Nicholas / Campbell, Kevin / Sikes, Travis et al. | AIAA | 2017