The invention discloses high-nitrogen steel with high and low temperature toughness. The high-nitrogen steel is prepared from chemical components in percentage by mass: 21.2%-21.8% of Cr, 16.8%-17.5% of Mn, 0.5%-0.85% of Mo, 1.5%-2.0% of Ni, 0.01%-0.1% of Si, 0.02%-0.05% of C, 0.5%-1.0% of N, 0.001%-0.003% of S, 0.016%-0.02% of P and the balance of Fe and inevitable impurities. The nickel content is reduced to a certain extent, and meanwhile, high low-temperature toughness is achieved.

    本发明公开了一种具有高低温韧性的高氮钢,其化学成分的质量百分比为Cr 21.2~21.8%、Mn 16.8~17.5%、Mo 0.5~0.85%、Ni 1.5~2.0%、Si 0.01~0.1%、C 0.02~0.05%、N 0.5~1.0%、S 0.001~0.003%、P 0.016~0.02%,余量为Fe和不可避免的杂质。本发明在一定程度上降低镍含量的同时具有高的低温韧性。


    Access

    Download


    Export, share and cite



    Title :

    High-nitrogen steel with high and low temperature toughness and preparation method thereof


    Additional title:

    一种具有高低温韧性的高氮钢及其制备方法


    Contributors:
    MIAO QIUXIA (author)

    Publication date :

    2021-11-26


    Type of media :

    Patent


    Type of material :

    Electronic Resource


    Language :

    Chinese


    Classification :

    IPC:    C22C Legierungen , ALLOYS / B63B Schiffe oder sonstige Wasserfahrzeuge , SHIPS OR OTHER WATERBORNE VESSELS



    Development of a high strength high toughness ausferritic steel

    Putatunda, Susil K. / Singar, Arjun V. / Tackett, Ronald et al. | Tema Archive | 2009


    High-toughness high-brightness black air inlet grille and preparation method and application thereof

    LIU QIANG / HUANG DONG / TANG WEI et al. | European Patent Office | 2023

    Free access

    Preparation method of ultrahigh-temperature ceramic material with high bending strength and fracture toughness

    ZHEN QIANG / LI JIAXI / ZHENG FENG et al. | European Patent Office | 2024

    Free access

    High-strength and high-toughness high-speed rail brake steel back

    WU HOUYU | European Patent Office | 2020

    Free access

    Development of high toughness bainitic microalloyed forging steel

    Nakamura,S. / Inoue,K. / Hanyuda,T. et al. | Automotive engineering | 1998