For the TC17 titanium alloy, the influence of the leading end angle of the mandrel on the expansion strengthening effect of the hole structure was studied, the surface integrity of the hole expansion strengthened under different process parameters was characterized, the high temperature and low cycle of the original and strengthened samples were tested. Fatigue life and the morphological characteristics of fatigue fracture are analyzed. The results show that the lead angle of the mandrel has a significant effect on the surface roughness after expansion. The uneven plastic flow of the metal on the surface of the hole wall during the expansion process leads to uneven residual stress distribution on the hole wall after expansion, and the residual stress amplitude at the exit end of the expansion is the largest, and the hole wall has a certain depth of residual compressive stress gradient field after expansion. When the interference of the core rod is constant, the fatigue life increases with the increase of the rear lead end angle of the mandrel. When the rear lead end angle is 8°, the median fatigue life gain after strengthening can reach 1.74 times, and the strengthening effect is the best, its minimum cycle life is 16331 times, which is higher than the longest cycle life of the original sample (13965 cycles). After strengthening, the origin of the cracks is changed from the multi-source type in the middle of the hole wall to the single-source crack initiation at the inlet end of the expansion.


    Access

    Download


    Export, share and cite



    Title :

    Effect of lead angle of hole expansion mandrel on surface integrity and fatigue performance of TC17 titanium alloy hole structure


    Contributors:
    MA Shicheng (author) / WANG Xin (author) / SONG Yinggang (author) / WANG Qiang (author) / LUO Xuekun (author) / XU Chunling (author) / TANG Zhihui (author)


    Publication date :

    2021




    Type of media :

    Article (Journal)


    Type of material :

    Electronic Resource


    Language :

    Unknown




    Effect of Cold Expansion on Fatigue Life of Hole Structure of TC17 Titanium Alloy

    AI Yingjun / WANG Xin / SONG Yinggang et al. | DOAJ | 2017

    Free access

    Effect of High-Speed Milling Parameters on Surface Metamorphic Layer of TC17 Titanium Alloy

    TAN Liang / ZHANG Dinghua / YAO Changfeng | DOAJ | 2017

    Free access

    Effect of Double Cold Expansion of Hole on Fatigue Property of TB6 Titanium Alloy

    LUO Xuekun / AI Yingjun / WANG Xin et al. | DOAJ | 2017

    Free access

    Effect of Twice Hole Expansion on Fatigue Property of Ti1023 Alloy

    YANG Guangyong / LI Meng / SONG Yinggang et al. | DOAJ | 2016

    Free access

    Numerical Simulation of TC17 Titanium Alloy Thin Blade Strengthened by Laser Shock Processing

    Ma, Sijie / Ding, Xiangyu / Yang, Zhi et al. | Springer Verlag | 2022