The effect of temperature on surface oxidation characteristics of nickel-base superalloy GH4169 powder was investigated by field emission scanning electron microscope (FE-SEM),energy-dispersive spectroscopy (EDS),X-ray photoelectron spectroscopy (XPS) and secondary ion mass spectrometry (SIMS). The results show that the surface of the GH4169 superalloy powder is partially oxidized at room temperature(RT),and on the surface there are elemental states dominated by Ni,Cr,Ti and Nb, and hydroxide/oxide dominated by Ni(OH)2,Cr2O3,TiO2 and Nb2O5。With the temperature increasing (150~250 °C) ,the peaks of Ni,Cr,Ti and Nb elements become weaker,the degree of oxidation is slightly increased and the surface of powder is partially oxidized. When the temperature reaches to 350 °C, the peaks of Ni,Cr,Ti,and Nb elements are all disappeared,and the surface of powder is fully oxidized. The oxide layer thickness is about 5 nm, and is mainly composed of Ni(OH)2,Cr2O3,TiO2and Nb2O5. The effect of temperature on oxidation characteristics of the GH4169 superalloy powder is significant,and the maximum treatment temperature of the GH4169 superalloy powder used for this study is no more than 250 °C exposed within 1 h under atmospheric conditions.


    Access

    Download


    Export, share and cite



    Title :

    Surface oxidation characteristics of nickel-base superalloy GH4169 powder


    Contributors:
    Zhang Lichong (author) / Xu Wenyong (author) / Li Zhou (author) / Wang Shuangxi (author) / Shen Jiankun (author) / Zheng Liang (author) / Zhang Guoqing (author)


    Publication date :

    2020




    Type of media :

    Article (Journal)


    Type of material :

    Electronic Resource


    Language :

    Unknown





    Effect of Surface Integrity of Turned GH4169 Superalloy on Fatigue Performance

    WU Daoxia / ZHANG Dinghua / YAO Changfeng | DOAJ | 2017

    Free access

    Formation Mechanism of Surface Metamorphic Layer on Turning End Face of GH4169 Superalloy

    YAO Changfeng / SHEN Xuehong / ZHANG Dinghua | DOAJ | 2017

    Free access

    Nickel-base superalloy

    Emerald Group Publishing | 1998


    Wrought nickel-base superalloy

    Miner, R. V. / Harf, F. H. / Kent, W. B. | NTRS | 1978