Based on the three-point bending test, the bending performances of S6C10-800/AC318 composite unidirectional plates with different span-thickness ratios (hereinafter referred to as unidirectional plates) were tested, and the effect of span-thickness ratio on the bending strength and bending modulus of unidirectional plate was studied. The influence and fracture mode of the specimens with different span-thickness ratios were analyzed to obtain the bending failure mechanism, and the critical span-thickness ratio of three-point bending test of unidirectional plate was determined. The results show that the bending strength of the unidirectional plate increases with the increase of the span-thickness ratio, and the bending modulus first increases and then decreases with the increase of the span-thickness ratio. The fracture mode of the unidirectional plate changes when the span-thickness ratio α=20, and the degree of delamination damage of unidirectional plate gradually decreases with the increase of span-thickness ratio, but the degree of splitting increases. When α≤20, the stress-strain curve conforms to the linear relationship with the increase of the span-thickness ratio, but when α>20, the stress-strain curve does not conform to the linear relationship. Therefore, the predicting formula of bending strength of unidirectional plate under arbitrary span-thickness ratio and a failure criterion for three-point bending test of unidirectional plate are obtained. It is recommended that the critical span-thickness ratio of the three-point bending performance test of unidirectional plate is 20. This is of great significance for optimizing the three-point bending test method of glass fiber composite materials to more accurately test the bending performance of composite materials.


    Access

    Download


    Export, share and cite



    Title :

    Effect of span-thickness ratio on bending properties of high-strength glass fiber reinforced composite unidirectional plate


    Contributors:
    BAI Xin (author) / WANG Yunying (author) / WANG Yana (author) / CHEN Xinwen (author) / HE Yuhuai (author)


    Publication date :

    2022




    Type of media :

    Article (Journal)


    Type of material :

    Electronic Resource


    Language :

    Unknown





    Anti-falling high-strength easily-connected glass fiber reinforced plastic flat plate

    YU XIANFEI / YOU SHANMEI | European Patent Office | 2024

    Free access

    EXPERIMENTAL BEND-TWIST COUPLING PROPERTIES OF THREE UNIDIRECTIONAL FIBER-REINFORCED COMPOSITE MATERIALS

    Walsh, J. / Walrath, D. / American Institute of Aeronautics and Astronautics | British Library Conference Proceedings | 2011



    High-strength detachable glass fiber reinforced plastic grating

    REN WENBIN / REN WENZHUO / ZHOU PENGFEI et al. | European Patent Office | 2021

    Free access