The time-to-corrosion initiation (Ti) of reinforcement and the chloride threshold content (Cth) of a series of G109 concrete slabs were experimentally investigated. Results indicate that Ti is increased by decreasing water-to-cement ratio or increasing cement alkalinity. The effects of a superplasticizer on initiation of corrosion of reinforcing steel bars (rebar) depend on concrete mix. Measurements reveal that chloride contents at both active (anodic) and passive (cathodic) sites increase linearly with the logarithm of Ti regardless of concrete mix, whereas chloride contents measured at anodic sites are always greater than at cathodic sites. Defects at or nearby corrosion anodic spots could facilitate chloride accumulation: rebar corrosion would occur earlier than if no defect were present. Further analysis reveals that the weakest-link theory is applicable to predict the probability of initiation of rebar corrosion, as indicated by the Weibull distributions of Ti and Cth.


    Zugriff

    Download

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effects of Concrete Mix on Initiation of Reinforcement Corrosion and Chloride Threshold Level


    Weitere Titelangaben:

    Transportation Research Record: Journal of the Transportation Research Board


    Beteiligte:
    Yu, Hui (Autor:in) / Lu, Baotong (Autor:in) / Presuel-Moreno, Francisco (Autor:in) / Zheng, Wei (Autor:in)


    Erscheinungsdatum :

    01.01.2011




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch