Early-age cracking can adversely affect the behavior and durability of bridge deck concrete. Cracking of hardening concrete occurs when the induced tensile stress exceeds the tensile strength of the concrete. The development of in-place stresses is affected by the shrinkage, modulus of elasticity, coefficient of thermal expansion, setting characteristics, restraint conditions, stress relaxation, and temperature history of the hardening concrete. Tensile strength increases as the hydration of the cementitious system progresses. Rigid cracking frame (RCF) testing techniques capture the combined effects of modulus of elasticity, creep and relaxation, coefficient of thermal expansion, thermal conductivity, autogenous shrinkage, and tensile strength on the cracking potential of a mixture in a specific application. This paper describes an experimental evaluation of the effect of supplementary cementing materials, water-to-cement ratio (w/c), and placement temperature conditions on the early-age cracking tendency of bridge deck concrete through the use of RCF testing techniques. Specimens were tested under temperature conditions that match those in an 8-in.-thick bridge deck to explore early-age cracking mechanisms. The laboratory testing program revealed that the placement temperature and curing temperature significantly affected the time to cracking of all the mixtures. Use of either fly ash or ground-granulated blast-furnace slag was effective in reducing the heat generation and rate of stiffness development in bridge deck concretes and thus in significantly reducing restraint stresses and delayed the occurrence of cracking at early ages. A decrease in w/c resulted in increased stresses, and it accelerated the occurrence of cracking at early ages.


    Zugriff

    Download

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Cracking Tendency of Bridge Deck Concrete


    Weitere Titelangaben:

    Transportation Research Record


    Beteiligte:


    Erscheinungsdatum :

    2010-01-01




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch



    Cracking Tendency of Bridge Deck Concrete

    Byard, Benjamin E | Online Contents | 2010


    How to Avoid Premature Bridge Deck Cracking

    British Library Online Contents | 1992


    Development of a Specification for Low-Cracking Bridge Deck Concrete in Virginia

    Nair, Harikrishnan / Ozyildirim, H. Celik / Sprinkel, Michael M. | Transportation Research Record | 2017


    Polymer-Concrete Bridge Deck Overlays

    Doody, Michael E. | Online Contents | 1994


    Concrete Bridge Deck Quality Mapping with Seismic Methods

    McDaniel, Mark / Celaya, Manuel / Nazarian, Soheil | Transportation Research Record | 2010