Critical fatigue safety state is investigated on RD2 type axle of China railway freight cars. Attention is paid on the grooves near axle boxes, where more fatigue cracks were early appeared even result in at least six derailed accidents. Load history was obtained by vehicle dynamics simulation combining with on-line inspection. Braking loads and effects of maintenance and off-round of wheels are also incorporated. Semi-elliptical and external circumferential cracks are employed for crack growth simulation. Crack shape change and shear stressing of the semi-elliptical crack are taken into account. New crack growth rate modeling in which covers from cracking threshold to toughness related fracture state is applied for residual life evaluation. Critical fatigue safety state is defined as the crack size from which the axle can be safely operated to next overhaul inspection. Critical crack size is estimated step-by-step with the crack shape change. Results show that the external circumferential crack is more dangerous than the semi-elliptical crack. Application more than two years in production verifies that the present assessment is available and reliable.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Probabilistic Critical Fatigue Safety State of the RD2 Type Axle of China Railway Freight Car



    Erschienen in:

    Erscheinungsdatum :

    12.06.2008


    Format / Umfang :

    8 pages




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Fatigue Reliability Research on RD2 Axle of Railway Freight Car

    Yang, Bing ;Zhao, Yong Xiang | Trans Tech Publications | 2007


    Fatigue Reliability Research on RD~2 Axle of Railway Freight Car

    Yang, B. / Zhao, Y.X. | British Library Conference Proceedings | 2007


    Probabilistic Critical Safety Wheel Wear Sizes of Chinese Railway Freight Cars

    Zhao, Yong Xiang ;Yang, Bing ;Feng, Ming Fei | Trans Tech Publications | 2008


    Probabilistic Modelling of Fatigue Crack Growth in Railway Axle

    Yasniy, O. / Pyndus, Y. / Sorochak, A. et al. | Tema Archiv | 2010


    Design review of a freight railway axle: fatigue damage versus damage tolerance

    Beretta, S. / Carboni, M. / Cervello, S. | Tema Archiv | 2011