U71Mn is the main steel grade for high-speed railway rails. In the production of U71Mn rail, its decarburization depth is the deepest, and the qualified percentage is lower than 60% for the requirement of less than 0.3mm of decarburization depth. On the basis of current heating furnace, the influence of different heating processes on the decarburization depth of U71Mn rail was studied, and the result shows that just optimization of heat process can not decrease greatly the decarburization depth. Therefore the high temperature anti-oxidation coating protection technology was carried out in the process of heating of U71Mn rail. Under the condition of protection heating and optimization of heating process, the decarburization depth of U71Mn rail decreases significantly, and the qualified rate reaches to more than 95% for the depth of less than 0.30mm, and 100% for the depth of less than 0.50mm.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Decarburization Depth Control Technology Research and Application for U71Mn Rail



    Erschienen in:

    Advanced Materials Research ; 774-776 ; 1181-1185


    Erscheinungsdatum :

    04.09.2013


    Format / Umfang :

    5 pages




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch





    Simulation Study on High-Speed Milling Performance of Rail U71Mn Material

    Pan, Chao / Zhang, Jianqiang / He, Yuelei et al. | British Library Conference Proceedings | 2018


    Analysis of the Generation Cause of Scale Shelling Defects on Running Surface of 60kg/m U71Mn Rail

    Zhou, Jian Hua ;Ji, Yu ;Ren, An Chao | Trans Tech Publications | 2011


    Methods of Measuring Decarburization

    SAE Technical Papers | 2018


    METHODS OF MEASURING DECARBURIZATION

    SAE Technical Papers | 1983