The effect on 22 Cr duplex stainless steel of coupling to carbon-steel in acid brine environments at 80 deg C has been evaluated. At low charging currents, hydrogen uptake was independent of pH and H2S and proportional to the square root of the charging current density. At higher charging currents, a critical value was reached above which hydrogen uptake was independent of the charging current density in H2S-free solution. In H2S environments, hydrogen uptake remained proportional to the square root of the charging current density and independent of the concentration of H2S. No significant reduction in the strain-to-failure relative to oil was observed in H2S-free environments. Pre-exposure for 50 days had only a modest effect on the strain-to-failure. In H2S environments, cracking may occur at coupling currents greater than 100 x 10-6 A/cm2.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Performance of duplex stainless steels in oilfield environments


    Beteiligte:
    Griffiths, A.J. (Autor:in) / Turnbull, A. (Autor:in)


    Erscheinungsdatum :

    1997


    Format / Umfang :

    4 Seiten, 2 Bilder, 5 Quellen



    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Duplex stainless steels for offshore use

    Bendall, K. | Tema Archiv | 1992


    Duplex stainless steels for chemical tankers

    Charles, J. / Vincent, B. | Tema Archiv | 1997



    Lean duplex stainless steels for structural applications

    Doble, Olaf / Havn, Torfinn | Tema Archiv | 2007


    About Sintering and Properties of Duplex Stainless Steels

    Rosso, M. / Actis-Grande, M. / Motoiu, P. et al. | British Library Conference Proceedings | 2001