For high performance aerospace structures, the properties of highest priority are low density, high strength, and high stiffness (modulus of elasticity). Addition of beryllium decrease the density of the aluminium alloy and increase the strength and the stiffness of the alloy. However it is very difficult to produce the Al-Be alloy having useful engineering properties by conventional ingot casting, because of the extremely limited solid solubility of beryllium and aluminium. So, rapid solidification processing is necessary to obtain extended solid sulubility. In this study, rapidly solidified Al-6 at% Be alloy were prepared by twin roll melt spinning process and single roll melt spinning process. Twin roll melt spun ribbons were extruded at 450 deg C with reduction in area of 25:1 after vacuum hot pressing at 550 deg C and 375 deg C. The microstructure of melt spun ribbon exhibited a refined cellular microstructure with dispersed Be particles. As advance velocity of liquid/solid interface increase, the morphology of Be particle vary from rod-like type to spherical type and the crystal structure of Be particle from HCP to BCC. These microstructural characteristics of rapidly solidified Al-6 at% Be alloy were described on the basis of metastabile phase diagram by Perepezko and Boettinger. The extruded ribbon consisted of recrystallized grains dispersed with Be particles and exhibited improved tensile property compared with that of extruded ingot.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Microstructure and tensile property of rapidly solidified Al-Be alloy


    Weitere Titelangaben:

    Mikrogefüge und Zugeigenschaften von schnell erstarrten Al-Be-Legierungen
    Titel koreanisch


    Beteiligte:
    Lee, In-Woo (Autor:in) / Park, Hyun-Ho (Autor:in) / Kim, Myung-Ho (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    1995


    Format / Umfang :

    10 Seiten, 9 Bilder, 1 Tabelle, 10 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Koreanisch






    Microstructure and Grain Refining Performance of a Rapidly Solidified Al-5Ti-1B Master Alloy

    Han, Y. F. / Shu, D. / Jin, L. et al. | British Library Conference Proceedings | 2007


    Fretting Fatigue Analysis in Rapidly Solidified Powder Aluminum Alloy

    Itou, Y. / Hotta, S. / Saruki, K. et al. | British Library Conference Proceedings | 1998


    Fretting fatigue analysis on rapidly solidified powder aluminium alloy

    Itou,Y. / Hotta,S. / Saruki,K. et al. | Kraftfahrwesen | 1998