Two types of stainless steel were exposed to the alternate conditions of 1 h immersion in chloride-containing solution and 7 h drying at 30 degree C and 67% RH. The corrosion rates and corrosion potentials were monitored simultaneously and continuously during exposure by using combined AC impedance and corrosion potential monitoring techniques in order to study the mechanism of pitting corrosion of stainless steels under a marine atmospheric environment. The results show that pitting is initiated preferentially during the dry cycle after a critical chloride concentration is reached. Pit initiation is followed by a shift of the corrosion potential to about -400 mV (SSE) as growth commences. Afterwards, as the specimen surface dries up, repassivation commences, and it may continue towards the next wet cycle if perfect drying within the active pit is not permitted. Furthermore, it was found that the presence of thin solution layers in atmospheric corrosion contributes to the enhancement of pit initiation and growth. A mechanism was proposed to explain the pitting corrosion of stainless steel in a marine atmospheric environment.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Pitting corrosion mechanism of stainless steels under wet-dry exposure in chloride-containing environments


    Beteiligte:
    Cruz, R.P.V. (Autor:in) / Nishikata, A. (Autor:in) / Tsuru, T. (Autor:in)

    Erschienen in:

    Corrosion Science ; 40 , 1 ; 125-139


    Erscheinungsdatum :

    1998


    Format / Umfang :

    15 Seiten, 10 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Investigation of pitting corrosion behaviour of welded duplex stainless steels

    Gobbon,M.E. / Univ.d.Bundeswehr Hamburg,DE | Kraftfahrwesen | 1994


    Pitting corrosion and crevice corrosion behaviors of high nitrogen austenitic stainless steels

    Li, H. b. / Jiang, Z. h. / Yang, Y. et al. | British Library Conference Proceedings | 2009



    Stainless steels in road environments

    Olsson, Anders / Olsson, Jan / Bergquist, Arne et al. | Tema Archiv | 2007


    Mechanism of dissimilar metal crevice corrosion of superferritic stainless steels

    Salamat, G. / Juhl, G.A. / Kelly, R.G. | Tema Archiv | 1995