A study was conducted to examine the effects of selected alloy constituents, particularly copper and iron in greater detail to more closely monitor define their effects on filiform corrosion behavior. Apart from filiform corrosion on painted samples, the corresponding corrosion behavior of unpainted samples was also evaluated to determine whether or not the same effects of alloy constituents on filiform performance were observed on more general corrosion behavior, such as pitting. Painted and unpainted samples were tested. Testing consisted of 6 hours exposure to copper acidified salt spray followed by four weeks at 60 C, 85% relative humidity. After corrosion testing, the unpainted samples were cleaned using the ASTM G1 procedure to remove corrosion products. The results show that the corrosion behavior of unpainted specimens in terms of maximum pit depth exhibit the same general trends as filiform corrosion of painted samples.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Aluminum wheel alloy variants: effects on corrosion performance


    Beteiligte:
    Courval, G.J. (Autor:in) / Chamberlain, B. (Autor:in) / Pattemore, D. (Autor:in)


    Erscheinungsdatum :

    1998


    Format / Umfang :

    8 Seiten, 8 Quellen



    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Aluminum Wheel Alloy Variants: Effects on Corrosion Performance

    Chamberlain, B. / Pattemore, D. / Courval, G.J. | SAE Technical Papers | 1998


    Aluminum wheel alloy variants: effects on corrosion performance

    Courval,G.J. / Chamberlain,B. / Pattemore,D. et al. | Kraftfahrwesen | 1998


    WHEEL COVER OF ALUMINUM ALLOY WHEEL

    HSIEH FU-YUAN | Europäisches Patentamt | 2018

    Freier Zugriff

    Aluminum alloy coating, aluminum alloy wheel hub and spraying method of aluminum alloy wheel hub

    HAN PENG / WEI QINGWANG / SONG YAFEI et al. | Europäisches Patentamt | 2023

    Freier Zugriff

    Commercial aluminum alloy wheel

    NI QING | Europäisches Patentamt | 2021

    Freier Zugriff