This paper deals with the problem of the fracture of composite to metal adhesive joints subject to thermo-mechanical loading. The problem is analyzed using a fracture mechanics model, which predicts the critical temperature change at which fracture occurs for a given pair of materials as a function of their thickness ratio. The experimental program carried out to verify the analytical results is described. Thermal tests were conducted on single and double lap joints of metal adhesively bonded to composite. The fracture resistance of the adhesive joint was measured by mechanical testing. It was observed that the steady-state fracture mechanics analysis correctly predicted trends in the critical temperature drop to cause failure as a function of adherend properties. The mechanical tests revealed that scrim-reinforced film adhesives can exhibit resistance curve behavior. It was also noted that a single value of adhesive toughness is not sufficient to characterize fracture data.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fracture of composite-metal adhesive joints under thermo-mechanical loading


    Weitere Titelangaben:

    Bruch von Verbundstoff-Metall-Klebverbindungen unter thermomechanischen Belastungen


    Beteiligte:
    Shetty, S.P. (Autor:in) / Spearing, S.M. (Autor:in)


    Erscheinungsdatum :

    1997


    Format / Umfang :

    8 Seiten, 5 Bilder, 1 Tabelle, 13 Quellen



    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch






    Thermo-mechanical Stresses in Single-Lap Composite Adhesive Joints (AIAA 2015-1884)

    Kumar, S. | British Library Conference Proceedings | 2015


    The reliability of adhesive joints under piezomechanical loading

    Sanders, Catherine / Spearing, S. / Shaw, Michael | AIAA | 2000


    The Reliability of Adhesive Joints Under Piezomechanical Loading

    Sanders, C. / Shaw, M. / Spearing, S. M. et al. | British Library Conference Proceedings | 2000