Exfoliation and alternate immersion corrosion were investigated in Al alloy 2024-T3 (UNS A92024) uptake during exposure and to correlate it with corrosion characterization. Characterization involved determination of weight loss, pitting density, and maximum depth of attack. Hydrogen uptake was determined by subsequent hydrogen evolution during heating. In both accelerated corrosion tests, pitting developed into intergranular corrosion and intergranular attack. Hydrogen penetrated through Al 2024-T3. In the exfoliation test, hydrogen concentration correlated well with the increase in available surface area during intergranular attack. There was indirect evidence that the first portions of hydrogen absorbed were arrested chemically inside the specimen. Free hydrogen (which evolves with mild heating) started to build up only after all active sites were occupied.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Hydrogen absorption into aluminium alloy 2024-T3 during exfoliation and alternate immersion testing


    Weitere Titelangaben:

    Wasserstoffabsorption in die Aluminiumlegierung 2024-T3 während Schichtkorrosion- und Wechseltauchtest


    Beteiligte:

    Erschienen in:

    Corrosion, Houston ; 54 , 1 ; 73-78


    Erscheinungsdatum :

    1998


    Format / Umfang :

    6 Seiten, 8 Bilder, 13 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Exfoliation Corrosion Behavior of 2524 Aluminium Alloy

    Yang, S. / Yi, D. Q. / Yao, S. J. et al. | British Library Conference Proceedings | 2007



    Exfoliation Testing of Aluminum

    SAE Technical Papers | 1997


    DROP TOWER AND ALTERNATE IMMERSION MACHINE: DESIGN AND REVIEW

    Bender, M. / Lanning, D. / American Institute of Aeronautics and Astronautics | British Library Conference Proceedings | 2011


    Drop Tower and Alternate Immersion Machine: Design and Review

    Bender, Matt / Lanning, David | AIAA | 2011