In-field repair of composite air craft is often performed in difficult conditions and hence needs to be as simple as possible. Current repair techniques generally involve the application of composite patches based on thermosetting epoxy resin via either wet lay-up, prepreg stacking over a film adhesive, or bonding precured patches. These methods of repair are very effective, but a complex cure cycle under controlled conditions is required and the use of epoxy resin means that storage must be taken into consideration. Composite patches based on thermoplastic resins overcome both of these problems; they do not require curing, and have no special storage neeeds. Thermoplastics can also be thermoformed and can hence be produced in sheet form and formed to the correct shape in situ during adhesive bonding to the surface to be patched, using vacuum and heat. With its low thermoforming temperature and good mechanical properties, polycarbonate is a goood candidate for use as a thermoplastic matrix, with woven carbon fibre fabric as the reinforcement to produce patch laminates. The present paper describes the use of solution impregnation together with film stacking to produce patches of acceptable quality and how these patches were formed without any wrinkling using double diaphragm forming. It was shown that thermofoming of polycarbonate based laminates can be performed at lower temperatures than those previously reported, with forming beginning between 140 and 150 deg C when a heater mat and vacuum bag were used. To avoid wrinkles double diaphragm forming was used as an effective method to produce well formed polycarbonate/ carbon fibre laminates.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fabrication of woven carbon fibre/polycarbonate repair patches


    Weitere Titelangaben:

    Herstellung von Ausbesserungsfpflastern aus gewebten Carbonfasern in Polycarbonat


    Beteiligte:
    Smith, F.C. (Autor:in) / Moloney, L.D. (Autor:in) / Matthews, F.L. (Autor:in) / Hodges, J. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    1996


    Format / Umfang :

    7 Seiten, 5 Bilder, 7 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Residual Thermal Stresses Around Bonded Fibre Metal Laminate Repair Patches on an Aircraft Fuselage

    Vlot, A. / Soerjanto, T. / Yeri, I. et al. | British Library Conference Proceedings | 1996



    Bonded Fiber Metal Laminate Repair Patches

    Vlot, A. / Guijt, C. / Greer, J. et al. | British Library Conference Proceedings | 1999


    Application of PTFE woven fibre

    Emerald Group Publishing | 1974


    OPTIMAL SHAPE OF REPAIR PATCHES IN COMPOSITES

    Echer, L. / De Souza, C. E. / Marczak, R. J. | British Library Conference Proceedings | 2018