The concept of repairing cracked aluminum aircraft structures with composite patches was investigated both analytically and experimentally. Coupon tests provided basic mechanical properties of composite patches manufactured using a repair procedure. A new surface treatment for bonding patches was developed and optimized. The damage repair process was substantiated by elements and beam testing. Crack growth predictions were made using analytical stress intensity factors for the patched structure, and excellent correlation was obtained between observed and predicted values. Patches were very effective in reducing the crack growth rate. Cracks of patched element specimens which propagated to failure during random spectrum fatigue loading survived without failure for much longer lifetimes (approx. 3.5 times) under all tested environmental conditions. The process was then substantiated by repairing and testing a defective beam element.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Repair of cracked aluminum aircraft structure with graphite/epoxy patches


    Weitere Titelangaben:

    Reparatur von gerissenen Aluminiumkonstruktionen in Flugzeugen mit Flecken aus graphitverstärktem Epoxidharz


    Beteiligte:
    Leibovich, H. (Autor:in) / Sasson, N. (Autor:in) / Simon, A. (Autor:in) / Green, A.K. (Autor:in)


    Erscheinungsdatum :

    1993


    Format / Umfang :

    8 Seiten, 7 Bilder, 1 Tabelle, 3 Quellen



    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch