The effect(s) of trace additions of Zn to the artificial aging behavior of alloy 8090 (Al-Li-Cu-Mg-Zr) was investigated in the approximate composition range 0-1 wt.% Zn. Trace Zn additions were found to delay aging and under equivalent aging treatments (100 hrs at 160 Cel) the alloy without Zn and the 1.07 wt.% Zn alloy developed delta prime-free zones along subgrain boundaries, while the alloys of 0.21 and 0.58 wt.% Zn did not. DSC analysis indicated that Zn was being incorporated into the delta prime, shifting it's exotherm to higher temperatures, while having little of any effect on its associated endotherm making it unlikely that it is an artifact of a solvus shift. In the 8090 + 1.07 wt.% Zn alloy, coarse precipitates were found to reside on subgrain boundaries and EDS indicated that they were rich in Cu and Zn. It was also noted that in the Zn containing 8090 varients, the S' precipitates were more coarse in size than the baseline 8090.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    The effect of trace additions of Zn of the precipitation. Behavior of alloy 8090 during artificial aging


    Weitere Titelangaben:

    Einfluß von Spurenzuschlägen von Zn auf die Kristallisationseigenschaften der 8090 Legierung während des künstlichen Alterns


    Beteiligte:
    Klimer, R.J. (Autor:in) / Stoner, G.E. (Autor:in)


    Erscheinungsdatum :

    1991


    Format / Umfang :

    13 Seiten, 8 Bilder, 1 Tabelle, 15 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    High Temperature Deformation Behavior of 8090 Al-Li Alloy

    Ha, T. K. / Chang, Y. W. / Minerals, Metals and Materials Society; Structural Materials Division; Non-ferrous Metals Committee | British Library Conference Proceedings | 1995


    High Temperature Load Relaxation Behavior of 8090 Al-Li Alloy

    Tae Kwon Ha / Young Won Chang / Pohang University of Science and Technology; Center for Advanced Aerospace Materials | British Library Conference Proceedings | 1993


    Effect of Microstructure on the Anisotropic Fatigue Behavior of Al-Li 8090 Alloy

    Park, K. J. / Lee, C. S. / Kim, N. J. et al. | British Library Conference Proceedings | 1993



    Effect of surface topography of 8090 Al-li alloy during abrasive waterjet peening process

    Qutaba, Syed / Asmelash, Mebrahitom / Azhari, Azmir | American Institute of Physics | 2024