The acoustic emission (AE) characteristics from the fatigue crack propagation in SM50B-Zc steel were strongly affected by the environment medium. The AE feature from the fatigue process both in air and in 3.5 % NaCl aqueous solution manifested a periodicity which indicated the fatigue extension was discontinuous. The fatigue striation and secondary cracking were main AE sources during the fatigue crack growth in air. In contrast, AE during the fatigue crack propagation in 3.5 NaCl solution was released from the intergranular fracture and quasicleavage cracking.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Acoustic emission monitoring the fatigue crack growth in SM50B-Zc steel for the structure of offshore platform


    Weitere Titelangaben:

    Schallemissionsanlage zur Überwachung der Ermüdungsrißausbreitung in dem für Bohrplattformen verwendeten Stahl SM50B-Zc


    Beteiligte:
    Wang Zhongguang (Autor:in) / Zhu Zuming (Autor:in) / Peng Jung (Autor:in)


    Erscheinungsdatum :

    1989


    Format / Umfang :

    8 Seiten, 14 Bilder, 1 Tabelle, 6 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch