In this paper an experimental analysis of Lamb waves interaction with riveted aluminum plates representative of aircraft splice joints submitted to fatigue tests is given. In this joint evaluation technique Lamb waves are excited and received outside the joint area using piezoelectric transducers bonded onto the plates. Detected damages are cracks in joint resulting from fatigue loading. These cracks lead to waveform transformations. This phenomenon is studied in this paper by considering the first derivative of the envelope of the time domain signal. The position of the first derivative curve maximum during cyclical loading gives information about crack development. It suggests, that monitoring the change in the delay of this maximum may provide a means of sizing the defects. By using X-rays, it was possible to measure the size of the cracks and compare it with delay evolution. Results are obtained for two types of fatigue sequences. It is experimentally shown that the relative delay measured is very sensitive to crack development. With the continued progress in the field of damage assessment techniques such as methods relying on Lamb waves, the safety of such structures can be ensured.
Lamb wave assessment of fatigue damage in aluminum plates
Abschätzung von Ermüdungsschäden in Aluminiumplatten mittels Lamb-Wellen
1999
11 Seiten, 19 Quellen
Aufsatz (Konferenz)
Englisch
Fatigue crack detection in metallic plates with non-linear Lamb wave modulation spectrum
Online Contents | 2010
|Fatigue crack detection in metallic plates with non-linear Lamb wave modulation spectrum
Emerald Group Publishing | 2010
|Impact of damage on propagation of Lamb waves in plates [3586-38]
British Library Conference Proceedings | 1998
|