The electrical and optical performance of 2.7 mil thick, 8 cm*8 cm silicon wrapthrough solar cells is described. These cells are desirable for spacecraft requiring lightweight, radiation resistant cells. Modeling of the radiation stability of BSF (back surface field) cells indicates that 80% of the power is retained after exposure to 6*1014 1 MeV electrons/cm2. Modeling performed on the beginning-of-life performance yields an ideal efficiency of 14% for the BSF and 14.7% for the BSFR (back surface field with reflector) cells. The best BSF and BSFR cell efficiencies measured are 13.7% and 14.1%, respectively, at AM0 28 degrees C. It is shown that the difference between the ideal and actual performances is due to series resistance and a higher than expected back surface recombination velocity.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Development of 2.7 mil BSF and BSFR silicon wrapthrough solar cells


    Weitere Titelangaben:

    Entwicklung von 2,7 mil BSF und BSFR Silizium-Wrapthrough-Solarzellen


    Beteiligte:
    Mason, A.V. (Autor:in) / Kululka, J.R. (Autor:in) / Bunyan, S.M. (Autor:in) / Woods, L.M. (Autor:in)


    Erscheinungsdatum :

    1990


    Format / Umfang :

    5 Seiten, 3 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    Silicon Solar Cells

    Wenham, S.R. | Online Contents | 1996


    Development of both-side junction silicon space solar cells

    Tonomura, Yoshifumi | Online Contents | 2001


    Crystalline silicon solar cells

    Goetzberger, Adolf / Voss, Bernhard / Knobloch, Joachim | TIBKAT | 1998


    Flexible silicon solar cells

    Blakers, A.W. | Online Contents | 2009