The reliability of several soldered thick film Ag/Pd and Ag/Pt conductors under thermal cycle conditions is reported. Evaluations were made of the thermal cycled adhesion by wire peel tests, as well as the electrical reliability of soldered components. In some cases, the failure modes with the mounted components were at the conductor/substrate or conductor/solder interfaces, and agreed generally with peel test results. However, when components were soldered to Pd/Ag conductors, vertical cracks were often observed through the conductor at the edge of the solder fillet. These cracks did not agree with failure modes from peel tests. The tendency for vertical and interface cracks was significantly reduced with the use of a high adhesion, dense firing Pd/Ag composition. The use of severe shock thermal cycle profiles tended to generate more vertical cracks as well as conductor/substrate cracks compared to slower thermal cycle profiles. No vertical cracks or conductor/substrate cracks were observed with the Pt/Ag conductor because of the much slower rate of Sn intermetallic formation compared with Pd/Ag conductors. Failure modes with the Pt/Ag conductor were often in the solder near the conductor/solder interface.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Thermal cycle performance of Ag-bearing thick film conductors for automotive applications


    Weitere Titelangaben:

    Thermische Wechselbständigkeit von Ag-haltigen Dickfilmleitern für Anwendungen in der Autoindustrie


    Beteiligte:
    Yamamoto, K. (Autor:in) / Uchida, S. (Autor:in) / Kojo, H. (Autor:in) / Hara, H. (Autor:in) / Yamamoto, Y. (Autor:in) / Taylor, B.E. (Autor:in) / LaBranche, M. (Autor:in)


    Erscheinungsdatum :

    1992


    Format / Umfang :

    8 Seiten, 13 Bilder, 2 Tabellen, 13 Quellen



    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    High-reliability silver-bearing thick film conductors for automotive applications

    Yamamoto, K. / Abou, S. / Uchida, S. et al. | Tema Archiv | 1992


    Wirebonding on multilayer circuits for automotive applications using robust thick-film conductors

    Schubring, A.W. / Sarma, D.H.R. / Webster, M.E. | Tema Archiv | 1999


    Thick film pressure sensors for automotive applications

    DellAcqua,R. / DellOrto,G. / Vicini,P. et al. | Kraftfahrwesen | 1981


    Automotive Thick Film Temperature Sensors

    Montaron, Bernard | SAE Technical Papers | 1983


    Automotive thick film temperature sensors

    Montaron,B. / Renix Electronique,Toulouse,FR | Kraftfahrwesen | 1983