The bipolar LiAl/FeS2 battery is being developed to achieve the high performance and long cycle life needed for electric vehicle application. The molten-salt (400 deg C to 440 deg C operation) electrolyte composition for this battery has evolved to support these objectives. An earlier change to LiCl-LiBr-KBr electrolyte is responsible for significantly increased cycle life (up to 1000 cycles). Recent electrolyte modification has significantly improved cell performance; approximately 50 % increased power, with increased high rate capacity utilization. Results are based on power-demanding EV driving profile test at 600 W/kg. The effects of adding small amounts (1 mol-% to 5 mol-%) of LiF and LiI to LiCl-LiBr-KBr electrolyte are discussed. By cyclic voltammetry, the modified electrolytes exhibit improved FeS2 electrochemistry. Electrolyte conductivity is little changed, but high current density (200 mA/cm 2) performance improved by approximately 50 %. A specific feature of the LiI addition is an enhanced cell overcharge tolerance rate from 2.5 mA/cm2 to 5 mA/cm2. The rate of overcharge tolerance is related to electrolyte properties and negative electrode lithium activity. As a result, the charge balancing of a bipolar battery configuration with molten-salt electrolyte is improved to accept greater cell-to-cell deviations.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Modification of LiCl-LiBr-KBr electrolyte for LiAl/FeS2 batteries


    Weitere Titelangaben:

    Modifikation des Elektrolyten LiCl-LiBr-KBr für LiAl/FeS2 Batterien


    Beteiligte:
    Kaun, T.D. (Autor:in) / Jansen, A.N. (Autor:in)


    Erscheinungsdatum :

    1996


    Format / Umfang :

    13 Seiten, 9 Bilder, 13 Quellen




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch