The growth behavior of stress corrosion cracks of X8O pipeline steel in the underground water of acidic soil environments was investigated by a slow-rate-loading crack growth test, electrochemical polarization curves, electrochemical impedance spectroscopy, and scanning electron microscopy. Crack growth mechanism was mixed-controlled by both anodic dissolution and hydrogen involvement. Ductile cracking first occurred and crack growth was primarily based on the anodic dissolution mechanism. Crack propagation gradually changed from ductile cracking to brittle cracking. Crack growth rate significantly accelerated with decreasing solution pH; crack propagation followed a hydrogen-based mechanism during the quick crack propagation stage.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Growth behavior of stress corrosion cracks of X80 pipeline steel in underground water of acidic soil


    Beteiligte:
    Wang, X.Z. (Autor:in) / Liu, Z.Y. (Autor:in) / Ge, X. (Autor:in) / Zhan, X.L. (Autor:in) / Du, C.W. (Autor:in) / Li, X.G. (Autor:in)

    Erschienen in:

    Corrosion, Houston ; 70 , 9 ; 872-879


    Erscheinungsdatum :

    2014


    Format / Umfang :

    8 Seiten, Bilder, Tabellen, 16 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch