The previous paper studied the effect of the internal stress distribution in specimen thickness on CTOD. The critical CTOD tends to decrease in consequence of the internal stress distribution in specimen thickness in case that secondary stress is tension mode toward the crack. In estimating the critical CTOD to brittle fracture in structural component with large residual stress distribution, it is important to take account of that secondary stress effect. This paper presents the effect of weld residual stress on critical CTOD to brittle fracture at lower shelf temperature of standard fracture toughness test. Using single edge notched bend (SENB) and single edge notched tension (SENT) specimens with/without residual stress, the fracture toughness tests have been conducted at -60 °C. The effect of weld residual stress on critical CTOD to brittle fracture depends on critical CTOD level. The critical CTOD with residual stress is calculated by the superposition of δ or stress intensity factor based on Dugdale model. Moreover, the δ on secondary stress derived from residual stress field scarcely affects constraint loss correction because the stress field from residual stress falls within the small scale yield condition.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    The effect of weld residual stress on critical CTOD to brittle fracture at lower shelf temperature


    Weitere Titelangaben:

    Einfluss von Schweißnahtrestspannungen auf die kritische CTOD zu Sprödbruch bei Tieflagentemperatur


    Beteiligte:
    Sakimoto, Takahiro (Autor:in) / Igi, Satoshi (Autor:in) / Oi, Kenji (Autor:in) / Suzuki, Shinichi (Autor:in) / Ostby, Erling (Autor:in)


    Erscheinungsdatum :

    2013


    Format / Umfang :

    7 Seiten, 15 Bilder, 1 Tabelle, 7 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Datenträger


    Sprache :

    Englisch




    CTOD WELDED JOINT WITH EXCELLENT CTOD PROPERTIES OF WELD METAL

    SONG WOO HYUN / HWANG WON TAEK | Europäisches Patentamt | 2018

    Freier Zugriff


    A review of the CTOA/CTOD fracture criterion - Why it works

    Newman, Jr., J. / James, M. | AIAA | 2001


    A review of the CTOA/CTOD fracture criterion-why it works.

    Newman, J.C. jun. / James, M.A. | Tema Archiv | 2001