The 321 stainless steel was tested subjected to atomic oxygen (AO) exposure to investigate the effect of AO in LEO environment. The mass loss, miro-roughness, and surface hardness were measured. The chemical composition and microstructure in the exposed surface layer were analyzed using XPS and TEM technique. The results show that the AO has an erosion effect on the stainless steel in the range of thin surface layer, leading to increase of micro-roughness. The long term exposure to AO results in an increase in oxygen content of the surface layer, forming metallic oxide. At the same time, the martensite phase which does not exist in the 321 stainless steel before AO exposure was detected after AO exposure, resulting in distinct surface hardening. The oxidative stress should be one of the major reasons for the surface eroding and hardening induced by AO exposure.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Erosion effect of atomic oxygen on the 321 stainless steel


    Weitere Titelangaben:

    Erosion von rostfreiem Stahl 321 durch atomaren Sauerstoff


    Beteiligte:
    Liu, Y. (Autor:in) / Yang, J.Q. (Autor:in) / Dong, S.L. (Autor:in) / Zhang, L. (Autor:in) / Zhang, Z. (Autor:in)


    Erscheinungsdatum :

    2012


    Format / Umfang :

    6 Seiten, 9 Bilder, 2 Tabellen, 15 Quellen




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Datenträger


    Sprache :

    Englisch




    Erosion Effect of Atomic Oxygen on the 321 Stainless Steel

    Liu, Y. / Yang, J.Q. / Ye, Z.Y. et al. | British Library Conference Proceedings | 2013


    Atomic oxygen erosion phenomena

    Banks, Bruce / Rutledge, Sharon / Stueber, Thomas et al. | AIAA | 1997


    Atomic Oxygen Erosion Consideration for Spacecraft Materials Selection

    Whitaker, A. F. / Kamenetzky, R. R. / National Aeronautics and Space Administration | British Library Conference Proceedings | 1994


    Influence of Atomic Oxygen Exposure on Friction Behavior of 321 Stainless Steel

    Liu, Y. / Yang, J. / Ye, Z. et al. | Springer Verlag | 2012


    Method for preventing cavitation erosion of stainless steel propeller

    JEONG NAK SHIN / WOO IL GUK | Europäisches Patentamt | 2018

    Freier Zugriff