Crack failure of a 36 inch high pressure gas pipe observed during regular inspection of a station has been investigated and the results are presented in this paper. The crack, approximately one meter long, was initiated from a notch inside the hot tapped hole in a pipeline installed about 30 years ago. The study was conducted by reviewing the design history and construction data, visual inspection, pipe material characterization, stress and modal analysis by using finite element method. Investigations revealed that the valve, directly connected to the split tee, faced large dynamic periodic forces due to a pressure drop between two pipelines. Metallurgical evaluation of the pipe material by optical microscope and fractography of the crack surface by scanning electron microscopy indicated the presence of elongated inclusions in the steel microstructure together with some indications of fatigue fracture as a poorly formed sawtooth profile. Based on dynamic analysis, it was found that the first mode shape, the maximum displacement and, therefore, the maximum stress were exactly situated within the crack initiation zone. It was concluded that the notch effect in the hot tapped hole, the position of the supports under the split tee and the presence of a large periodic stress were responsible for the initiation and fatigue propagation of the crack in the gas pipe.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Failure analysis of a high pressure natural gas pipe under split tee by computer simulations and metallurgical assessment


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    2013


    Format / Umfang :

    14 Seiten, 14 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Novel split type metallurgical vehicle

    FENG JIJUN / WANG YONGKANG / SHEN JIAN | Europäisches Patentamt | 2020

    Freier Zugriff


    Metallurgical Analysis of Hydrotested 20-Inch Natural Gas Pipeline

    Mahajanam, Sudhakar / Garcia, Efrain / Riggs, Kenneth | TIBKAT | 2021


    Vertical Split Rim Failure Analysis in Railroad Wheels

    Sura, V.S. / Mahadevan, S. / American Society of Mechanical Engineers | British Library Conference Proceedings | 2010


    Metallurgical studies of deepwater pipeline laid by reeled pipe method

    Chen, E.Y. / Mehdizadeh, P. | Tema Archiv | 1978