A moving train subjects a rail cross section to many wheel passes and heat generation at the interface from bulk friction and microslip. Frictional heating at the interface causes the temperature of the contacting rail surface and wheel surface to rise. After the train has passed, the rail temperature drops to ambient till the next train arrives. Wheels, on the other hand, pick up the frictional heat input continuously and hence their steady state temperature could be much higher than that of the rail. A hot wheel provides an additional temperature rise at the rail surface. The accompanying thermal stresses and thermal softening may enhance the rail wear rate. This has been investigated in the present study. A ratchetting failure-based computer simulation has been employed to assess the wear rate of a pearlitic rail steel. It is found that the thermal stress effect on wear rate is only the modest, but thermal softening can enhance the wear rate by up to an order of magnitude for the conditions considered.
Modelling the effect of steady state wheel temperature on rail wear
Modellierung des Einflusses der Gleichgewichtsradtemperatur auf den Gleisverschleiß
Tribology Letters ; 49 , 1 ; 239-249
2013
11 Seiten, 12 Bilder, 3 Tabellen, 24 Quellen
Aufsatz (Zeitschrift)
Englisch
Non-steady state modelling of wheel-rail contact problem
Kraftfahrwesen | 2013
|Non-steady state modelling of wheel–rail contact problem
Taylor & Francis Verlag | 2013
|Wear modelling in rail–wheel contact
Tema Archiv | 2015
|Tema Archiv | 2003
|British Library Conference Proceedings | 2003
|