Ground gathering pipelines in a high flow-rate gas condensate field were seriously corroded and became perforation only after five months operation. The results of witnessed inspections and analysis showed that T-branch pipe, Elbow and weld were corroded most seriously. The main features of the corrosion were trench-like corrosion pits. In order to clarify the reasons for corrosion so seriously, XRD, SEM, EDS were used to test the film of sample which was taken from the field. The results showed that wall thinning of pipelines was mainly caused by CO2 corrosion combined with erosion and the corrosion product was mainly composed of FeCO3.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Corrosion Reason Analysis of Ground Gathering Pipelines in High Flow-Rate Gas Condensate Field


    Beteiligte:
    Cai, Rui (Autor:in) / Han, Yan (Autor:in) / Zhu, Shi-Dong (Autor:in) / Lin, Guan-fa (Autor:in) / Bai, Zhen-quan (Autor:in)


    Erscheinungsdatum :

    2012


    Format / Umfang :

    5 Seiten




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Assessing corrosion behavior of light hydrocarbon condensate pipelines

    Perdomo, J.J. / Gonzalez, J.J. / Viloria, A. | Tema Archiv | 1999


    Hydrodynamic modeling of three-phase flow in production and gathering pipelines

    Zaghioul, Jose / Adewumi, Michael / Ityokumbul, M. Thaddeus | Tema Archiv | 2008


    Transients in gas-condensate natural gas pipelines

    Zhou, Junyang / Adewumi, M.A. | Tema Archiv | 1998


    Analysis of DOT reportable incidents for gas transmission and gathering pipelines

    Vieth, P. H. / Rosenfeld, M. J. / European Pipeline Research Group et al. | British Library Conference Proceedings | 1995