Dense and uniform coatings of iridium (Ir), 5-7 µm in thickness, were deposited onto molybdenum (Mo) substrates by double glow plasma discharge in the temperature range of 800-850°C at 35 Pa. During deposition, the Mo substrate was biased at a voltage of-300 V while the 99.9% Ir target was at a bias voltage of 800 V. After deposition, the Ir coating was ablated using an oxyacetylene torch with a flame temperature of ~2000°C to determine the high temperature stability of the coated substrate. The morphology and microstructure of the Ir coating were observed using scanning electronmicroscopy while the composition and structure weremeasured using X-ray diffraction and energy dispersive spectroscopy. The thickness of the as deposited Ir coating was uniform and the interface between the coating and the substrate exhibited excellent adhesion with no evidence of delamination and cracks. After exposure to the flame, the surface of the as ablated coating presented imperfections including pores, bulges and cracks; however, the Ir coating retained sufficient adhesion to limit the weight loss of the Ir coated Mo substrate to 10 mg cm-² s-¹.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Oxidation of double glow plasma discharge coatings of iridium on molybdenum for liquid fuelled rocket motor casings


    Weitere Titelangaben:

    Oxidation von durch Doppel-Plasma-Glimmentladung hergestellten Iridium-Überzügen auf Molybdän für Gehäuse von mit flüssigem Brennstoff betriebenen Raketentriebwerken


    Beteiligte:
    Wang, J.M. (Autor:in) / Zhang, Z.W. (Autor:in) / Xu, Z.H. (Autor:in) / Lin, X. (Autor:in) / Wu, W.P. (Autor:in) / Chen, Z.F. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2011


    Format / Umfang :

    5 Seiten, 6 Bilder, 17 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Robotic NDE Inspection of Advanced Solid Rocket Motor Casings

    McNeelege, G. E. / Sarantos, C. / American Institute of Aeronautics and Astronautics et al. | British Library Conference Proceedings | 1994


    Free Vibrations of Rocket Motor Casings under Internal Pressure

    S. K. Radhamohan / Y. V. K. Sadasiva Rao / B. Prasad | AIAA | 1975


    Robotic NDE inspection of advanced solid rocket motor casings

    McNeelege, Glenn / Sarantos, Chris | AIAA | 1994


    Maruca: an early French navy liquid-fuelled rocket

    Robert, Jean / Serra, Jean-Jacques / Jung, Philippe | AIAA | 2006