Buried pipelines paralleling or crossing high voltage power line systems are often subjected to induced AC interference, which may cause serious corrosion risk. There have been many conclusions including size of coating defects, AC current density, etc. to estimate corrosion condition, but no industry standard evaluation criterion has been established. In this paper, the AC induced corrosion of coated pipeline was studied with coated specimens in simulated soil solution under various experimental conditions to determine the AC corrosion risk considering the cathodic protection, coating defects, AC current density, soil acidity/alkalinity, and the soil resistivity. It has been identified that failures in oil and gas transmission pipelines by destructive pitting may be caused by AC interference. Pitting corrosion was also studied in this paper by electrochemical measurements and AC corrosion mechanism was further analyzed. Specific morphology of characteristics of AC corrosion was observed by Scanning Electron Microscope (SEM) technical.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Study of AC corrosion on coated pipeline steel in simulated soil solution


    Beteiligte:
    Xu, Xin (Autor:in) / Xu, Lining (Autor:in) / Liu, Wei (Autor:in) / Lu, Minxu (Autor:in)


    Erscheinungsdatum :

    2011


    Format / Umfang :

    20 Seiten, 18 Bilder, 3 Tabellen, 7 Quellen



    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Susceptibility of welded X80 pipeline steel to corrosion in simulated soil solution

    Ren, C.Q. / Xian, N. / Wang, X. et al. | Tema Archiv | 2012


    Transgranular stress corrosion cracking of X-60 pipeline steel in simulated ground water

    Zhang, X.Y. / Lambert, S.B. / Sutherby, R. et al. | Tema Archiv | 1999


    AFM study of the corrosion of pipeline steel in organic compounds extracted from soil

    Yasakau, K.A. / Weber, C.R. / Rodrigues, L.M. et al. | Tema Archiv | 2008


    Evaluation of crack and simulated corrosion defects in an API X-60 gas pipeline steel

    Hosseini, A. / Cronin, D. / Plumtree, A. | Tema Archiv | 2010