The Inline Inspection (ILI) data indicated that corrosion has taken place inside the pipeline transporting the wet natural gas containing CO2 at very high temperature. The corrosion inhibitor at the injection rate of 0.47 Liter per MMSCFT (One Pint per MMSCFT) was injected into the pipeline to protect carbon steel from corrosion. The corrosion modeling results showed very high corrosion rate under the operating conditions. The severity of corrosion inside the pipeline detected by ILI was much lower than the corrosion prediction modeling results. The finding in this study showed the passivation film formed under the operating conditions at very high temperature reduced the general corrosion rate. However, addition of the corrosion inhibitor to the testing autoclaves reduced its protection, and increased corrosion rate. A corrosion inhibitor that is compatible with the passivation film is required to protect the pipeline. This study demonstrated how the laboratory data have supported the corrosion mitigation program for a field operation through exploring the mechanism of high temperature CO2 corrosion of carbon steel in a low total dissolved solids (TDS) brine.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Study of corrosion and inhibition of carbon steel in CO2 containing natural gas at high temperature


    Beteiligte:
    Sun, Hejian (Autor:in) / Sujatmiko, Muhdi (Autor:in) / Aulia, Mohamad (Autor:in) / Davis, Josh (Autor:in) / Hudgins, Roger (Autor:in)


    Erscheinungsdatum :

    2011


    Format / Umfang :

    13 Seiten, 12 Bilder, 2 Tabellen, 6 Quellen



    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    The Corrosion of Carbon Steel in High Temperature Water

    Mochizuki, Katsuki / Morita, Toshiki / Fukuda, Katsuya | TIBKAT | 1992



    Inhibition effect of thioglycolic acid on carbon dioxide corrosion of carbon steel

    Bilkova, K. / Hackerman, N. / Bartos, M. | Tema Archiv | 2004


    Inhibition of weld corrosion in flowing brines containing carbon dioxide

    Alawadhi, K. / Robinson, M. / Chalmers, A. et al. | Tema Archiv | 2008