Corrosion behaviour of N80 carbon steel in formation water containing CO2 was studied by polarization curve technique, electrochemical impedance spectroscopy, weight loss test, scanning electron microscope, and X-ray diffraction. Effects of temperature and acetic acid concentration on the corrosion behaviour of N80 carbon steel were discussed. The results showed that increasing temperature not only enhanced the dissolution of steel substrate, but also promoted the precipitation of FeCO3, the addition of acetic acid enhanced localized corrosion attack on N80 carbon steel. FeCO3 was the main corrosion product. And there was a transition region between CO2 corrosion control and HAc corrosion control.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Corrosion of N80 carbon steel in oil field formation water containing CO2 in the absence and presence of acetic acid


    Weitere Titelangaben:

    Korrosion des Kohlenstoffstahles N80 in CO2-haltigem Schichtwasser von Erdölfeldern in Ab- und Anwesenheit von Essigsäure


    Beteiligte:
    Zhu, S.D. (Autor:in) / Fu, A.Q. (Autor:in) / Miao, J. (Autor:in) / Yin, Z.F. (Autor:in) / Zhou, G.S. (Autor:in) / Wei, J.F. (Autor:in)

    Erschienen in:

    Corrosion Science ; 53 , 10 ; 3156-3165


    Erscheinungsdatum :

    2011


    Format / Umfang :

    10 Seiten, 10 Bilder, 2 Tabellen, 42 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch