A centre-notched small size tension test specimen was developed to evaluate the toughness against unstable brittle fracture from fatigue crack, which is initiated and propagated from the surface of the butt-welded joints of heavy-thick steel plates. Centre-notched small size tension test specimens were made from butt-welded joints of 70 mm heavy-thick steel plates and employed for the tests using this plate thickness as the specimen width. In this paper, the test results are evaluated and investigated. Fracture toughness value (Kid) against unstable brittle fracture from fatigue crack, which is initiated and propagated from the welded toe of butt-welded joint of 70 mm heavy-thick steel plates, was grasped by centrenotched small size tension test specimens using the plate thickness as the specimen width. When the tested electrogas-welded joint is applied to a large welded structure such as a mega-container ship, the allowable surface fatigue crack length along the welded bead is determined to be about 100 mm, when a nominal yield stress (460 N/mm2) is applied to the structure at -10 deg C (the lowest design temperature for ships in normal worldwide service). On the other hand, the allowable surface fatigue crack length in tested steel plate, investigated in another paper is determined to be 340 mm.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Study on fracture toughness of welded joints for heavy-thick steel plates by centre-notched small size specimen


    Weitere Titelangaben:

    Studie über Bruchzähigkeit von Schweißverbindungen für sehr dicke Stahlplatten mit zentral gekerbten kleinen Proben


    Beteiligte:
    Yajima, H. (Autor:in) / Watanabe, E. (Autor:in) / Jia, Z.M. (Autor:in) / Yoshimoto, K. (Autor:in) / Ishikawa, T. (Autor:in) / Funatsu, Y. (Autor:in)

    Erschienen in:

    Welding in the World ; 55 , 5/6 ; 84-92


    Erscheinungsdatum :

    2011


    Format / Umfang :

    9 Seiten, 19 Bilder, 3 Tabellen, 3 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch





    Fracture Toughness of Austenitic Welded Joints

    Timofeev, B. / Sorokin, A. / Kaunas University of Technology | British Library Conference Proceedings | 2007


    Inexpensive Fracture Toughness Testing of Welded Steel

    Walters, Carey L. / Coppejans, Okko J. / Hoogeland, Martijn | Springer Verlag | 2020


    Inexpensive Fracture Toughness Testing of Welded Steel

    Walters, Carey L. / Coppejans, Okko J. / Hoogeland, Martijn | TIBKAT | 2021


    Fracture toughness and safety assessment of X65 offshore pipeline welded joints

    Li, Zhang / Zhang, Yufeng / Huo, Lixing et al. | Tema Archiv | 2005