This paper reports on metallurgical characterisation of small cracks in pearlitic steels, using observations from both twin disc tests and rails removed from service, plus methods to determine three-dimensional (3D) aspects of such cracks. Tests to varying fractions of rolling contact fatigue (RCF) life have been assessed, based on twin disc tests where 'average 100% RCF life' has been defined by eddy current detection of cracks between 200 and 800 micron in depth. Contact surface features and microstructural alterations have been mapped against near-surface strain and compared with worn rail examinations. Initial crack growth along favourably aligned and strained, prior-austenite (PA) grain boundaries, particularly if the boundary contains pro-eutectoid (PE) ferrite, was found to be restricted or halted at the PA grain limit or where the boundary altered to be less-favourably aligned. For samples with up to 55% RCF life, initial crack propagation length was still less than the average PA grain size. 3D aspects of this early growth and the deformed PA grain shapes were found to be linked to ratcheting flakes and flake cracks on test disc and rail contact surfaces. The results have shown how initial RCF crack propagation is very microstructurally influenced.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Very early stage rolling contact fatigue crack growth in pearlitic rail steels


    Weitere Titelangaben:

    Erstes Stadium des Wälzermüdungsrisswachstums in perlitischen Radstählen


    Beteiligte:
    Garnham, J.E. (Autor:in) / Davis, C.L. (Autor:in)


    Erscheinungsdatum :

    2011


    Format / Umfang :

    13 Seiten




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Wear and Rolling Contact Fatigue Behavior in Pearlitic and Bainitic Rail Steels

    Yokoyama, H. / Mitao, S. / Yamamoto, S. et al. | British Library Conference Proceedings | 2001


    Integrated study of fatigue and wear of pearlitic rail steels under rolling-sliding contact conditions

    Beynon, J. H. / Brown, M. W. / Joyce, R. D. et al. | British Library Conference Proceedings | 2000