Due to the significance of the propagation of stress wave in composite armor during projectile-target interaction, the characteristics of stress wave propagation in multi-layered composite structure under impact load were investigated by traditional Split Hopkinson Pressure Bar system in this study. The effect of interlayer characteristic on the stress wave propagation was discussed. The results show that the interlayer properties between CMC (ceramic matrix composite) and RHA (rolling homogenous armor) steel play an important role in the propagation of wave. Compared to 'CMC/RHA' structure without interlayer, the tungsten carbide interlayer can increase stress level in CMC layer remarkably, while silica gel layer has an opposite effect, and epoxy resin adhesive layer has no distinct effect on the propagation of stress wave. The increased compressive stress level in CMC layer is very useful when the CMC layer served as the face plate of a composite armor. During the impact process of the projectile to the armor, the anti-penetration capability of the face plate of the composite armor can be improved when in the compression stress state. In the comparison ballistic testing conducted with 7.62 mm armor piercing projectiles, the protection efficiency of the 'CMC/WC/RHA' composite armor is about 36% higher than that of the 'CMC/RHA' structure, which is in good correlation with the stress wave measurement results.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of interlayer on stress wave propagation in CMC/RHA multi-layered structure


    Weitere Titelangaben:

    Einfluss einer Zwischenschicht auf die Fortpflanzung von Spannungswellen in einer CMC/RHA-Mehrschichtstruktur


    Beteiligte:
    Wang, Yangwei (Autor:in) / Wang, Fuchi (Autor:in) / Yu, Xiaodong (Autor:in) / Ma, Zhuang (Autor:in) / Gao, Jubin (Autor:in) / Kang, Xiaopeng (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2010


    Format / Umfang :

    5 Seiten, 8 Bilder, 1 Tabelle, 22 Quellen