For arctic pipeline systems, designers are required to deal with a number of unique environmental loading conditions not normally present in other regions of the world. For buried arctic onshore pipelines, the key structural design issue is the potential for high bending strains resulting from permafrost: frost heave and/or thaw settlement. Because of the lack of traditional design solutions to these unique deformation-controlled loading conditions, reliability-based limit state design methods are becoming increasingly preferred for arctic applications. They allow the integration of analytical and experimental assessments into the overall design philosophy, which has been shown to improve design concept confidence and reduce overall uncertainty. For a strain-based design approach, high pipeline bending strains due to deformation-controlled ground movements are addressed as a function of the defined allowable tensile and compressive strain limits. Excessive compressive strains may give rise to serviceability issues such as restricted pipeline pig passage or coating damage. In some cases, excessive compressive strains may compromise pipeline integrity due to other loads and could lead to ultimate limit state conditions associated with burst, fatigue or corrosion under damaged coating. To further develop the understanding of pipeline compressive strain capacity, this paper summarizes a test program performed at the C-FER (C-FER Technologies Inc.) testing facility in Edmonton, Canada, which quantified the critical compressive strain of 36-inch diameter, 19.8-mm wall thickness, grade X80 UOE (fabrication technique: from U-shape to O-shape to circumferential Expansion) linepipe. Test variables included heat treatment effects (simulated coating plant heating) and the presence of a girth weld. Work involved performing thermal treatment studies, material coupon tests and three full-scale bend tests on X80 UOE linepipe specimens subject to high internal pressure. As expected, the analysis of the results has shown that the presence of an offset in the girth weld reduced compressive strain capacity. It was also demonstrated that, although heat treatment increased the Y/T (yield to tensile) ratio, it did not have a significant impact on the slope of the stress-strain curve in the region where buckling occurred, thus resulting in no loss of local buckling capacity. Equations to predict critical buckling strain, which agree well with the full-scale test results, were formulated based on published work. These equations consider the influence of varying stress-strain curve shape.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Compressive strain limits of large diameter X80 UOE linepipe


    Weitere Titelangaben:

    Druckverformungsgrenzen von UOE-Leitungsrohren mit großem Durchmesser


    Beteiligte:


    Erscheinungsdatum :

    2009


    Format / Umfang :

    9 Seiten, 9 Quellen



    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Datenträger


    Sprache :

    Englisch




    Buckling resistance of large diameter spiral welded linepipe

    Zimmerman, Tom / Xie, Jueren / Timms, Chris et al. | Tema Archiv | 2004



    Strain capacity of X100 high-strain linepipe for strain-based design application

    Igi, Satoshi / Kondo, Joe / Suzuki, Nobuhisa et al. | Tema Archiv | 2008



    Linepipe welding beyond 2000

    Widgery, D.J. | Tema Archiv | 2000